Transparent Printed Polycarbonate Film/Sheet
Widely used in thin film switches, panels, signs, masks, instrument panels, automotive interiors and other products.
With HD transparency, good compression performance, high dimensional stability, excellent printing performance, easy processing and forming.
With HD transparency, good compression performance, high dimensional stability, excellent printing performance, easy processing and forming.
Product Application
Specifications
The Size can be customized
Typical Property Value
PROPERTY | Test Method | Units | Value |
Physical | |||
Specific Gravity | ISO 1183 | g/cm3 | ≥1.2 |
Light Transmission | ASTM D1003 | % | >89 |
Haze | ASTM D1003 | % | <0.5 |
Water Absorption Equilibrium,24 Hrs | ASTM D570 | % | ≤0.35 |
Mechanical | |||
Tensile Strength | ISO527 | Mpa | Broadwise≥55 Direction≥60 |
Tensile Modulus | ISO527 | Mpa | ≥2200 |
Flexural Modulus | ISO178 | Mpa | ≥90 |
Elongation-at-break | GB/T 1040.3 | % | ≥90 |
Temperature Resistance | |||
Vicat Softening Temperature | ISO306 | ℃ | ≥140 |
Thermal Expansivity | ISO11359 | /℃ | 6.5*10-5 |
Electriacl | |||
Permittivity | IEC60250 | -- | ≥3.0 |
Voltage test | IEC60243 (DC) | KV/mm | ≥30 |
Volume Resistivity | IEC60093 | Ω.cm | ≥1014 |
Surface Resistivity | IEC60093 | Ω | ≥1015 |
Note: The above figures are typical values obtained under standard methods and should not be construed as unsteady application conditions.